QIDI PPS-CF 3D Printer Filament

PPS-CF is a composite material made from carbon fiber-reinforced polyphenylene sulfide (PPS). The combination of PPS resin with carbon fiber imparts excellent properties to PPS-CF, including outstanding solvent resistance, corrosion resistance, heat resistance, and flame retardancy. Additionally, higher printing temperatures enhance the strength, rigidity, and dimensional stability of PPS-CF. When paired with the QIDI Plus4, it becomes a specialty engineering plastic capable of meeting the demands of unique and challenging applications.

Heat Resistance Up to 264℃

PPS-CF features a heat deflection temperature of up to 264°C at 0.45 MPa and can maintain continuous operation at temperatures above 200°C. Its superior heat resistance ensures excellent creep resistance, making PPS-CF an ideal choice for challenging industrial environments and high-temperature applications.

Excellent Flame-resistant

PPS-CF is rated UL-94 V-0 for flame retardancy, ensuring exceptional safety and reliability in key applications like electronics and automotive parts. Its outstanding durability provides lasting performance and confidence, even in the most challenging conditions.

Top-tier Mechanical Properties

PPS-CF integrates the rigidity of PPS polymers with the reinforcing power of carbon fibers, delivering superior stiffness, flexural strength, and tensile strength. Its outstanding dimensional stability and resistance to warping ensure that large-scale prints retain precision and remain distortion-free throughout production, making it perfect for high-precision applications.

	PET-CF	PA12-CF	PAHT-CF	PPS-CF
Bending Modulus	5345 MPa	3916 MPa	6727 MPa	7160 MPa
Bending Strength	114 MPa	114 MPa	144 MPa	142 MPa

Solvent and Chemical Resistance

PPS-CF exhibits excellent solvent and chemical resistance. At temperatures below 200°C, it is virtually insoluble in any solvent and demonstrates outstanding resistance to acids, alkalis, and salts under normal conditions. This makes PPS-CF an ideal choice for demanding environments where high chemical stability is essential.

Ultra-Low Water Absorption

PPS-CF has an extremely low moisture absorption rate of just 0.05%, ensuring that its mechanical and thermal properties remain stable even in humid conditions. This makes it an optimal choice for applications that demand high moisture resistance.

	Dry State	Wet State
Impact Strength - XY	27.8 kJ/m²	27.8 kJ/m²
Bending Strength - XY	142 MPa	142 MPa
Bending Strength - Z	36 MPa	36 MPa
Bending Modulus - XY	7160 MPa	7160 MPa

Accessory Compatibility

	Recommended	Not Recommended
Build Plate	QIDI PEI Plate, HF Plate, PC Plate and Smooth Plate	/
Hotend	Hardened Steel Nozzle ( 0.4 / 0.6 / 0.8 mm) Bimetal Nozzle ( 0.4 / 0.6 / 0.8 mm)	Brass/Copper plated Nozzle (0.2/0.4/0.6/0.8 mm)
Glue	Glue Stick/ 3D LAC adhesive spray	/

Recommended Printing Settings
Drying Settings (Blast Drying Oven)	100-140 °C，8-12 h
Printing and Keeping Container's Humidity	< 20% RH (Sealed, with Desiccant)
Nozzle Temperature	310-350 °C
Bed Temperature (with Glue)	100 °C
Printing Speed	30-100 mm/s

Physical Properties
Density	1.3 g/cm³
Vicat Softening Temperature	268 °C
Heat Deflection Temperature	242.7 °C
Melting Temperature	284 °C
Melt flow rate	50-60 g/10 min

Mechanical Properties
Tensile Strength	55-65 MPa
Breaking Elongation Rate	>4-8 %
Bending Modulus	7160 ± 280 MPa
Bending Strength	142 ± 5 MPa
Impact Strength	27.8 ± 2.3 kJ/m²

Downloads

Filament TDS

Filament MSDS

Printing Tips

1. Using higher values within these ranges can enhance the mechanical properties of the printed parts, especially in the Z-direction.
2. Higher temperatures within the drying range yield better results, but do not exceed 160°C to avoid damaging the spool.
3. To prevent the filament from absorbing moisture, use an airtight storage container with desiccant during printing.
For more details please refer to: Filament Guide on WIKI.

PPS-CF Filament